Walki®Bioska Film 506
Walki®Bioska Film 506 becomes self-adhesive when subjected to heat, so separate adhesive is not necessarily required during lamination. It can be laminated onto cardboard, cellulose-based products and a variety of compostable materials.
- meets the EN 13432 industrial compostability standard
- can be laminated onto cardboard, cellulose-based products and a variety of compostable materials
- durable even under demanding conditions, such as oils and salad dressings
- easy to use, seal and print on with flow-pack machines
Technical information
Our sales managers will gladly tell you more about the product properties.
|
Mitat
|
||||
|
Parametri
|
Standardi
|
Nimellisarvo
|
Yksikkö
|
Vaihteluväli
|
|
Paksuus
|
ISO 534
|
25
|
mic
|
+/- 10% |
|
Fyysis-mekaaniset ominaisuudet
|
||||
|
Parametri
|
Standardi
|
Nimellisarvo
|
Yksikkö
|
|
| Yksikköpaino |
ASTM D 2673
|
31,25
|
g/m27
|
|
|
Tiheys
|
ISO 1133
|
1,25
|
g/cm³
|
|
|
Kimmonmoduuli
|
ISO 527-3
|
MD |
4662
|
MPa
|
| CD |
408
|
MPa
|
||
|
Myötöraja
|
ISO 527-3
|
MD |
57,3
|
MPa
|
| CD |
54,0
|
MPa
|
||
|
Vetolujuus
|
ISO 527-3
|
MD |
83,1
|
MPa
|
| CD |
53,5
|
MPa | ||
|
Vetorasitus
|
ISO 527-3
|
MD |
2,64
|
mm/mm
|
| CD |
0,08
|
mm/mm
|
||
|
Murtoraja
|
ISO 527-3
|
MD |
2,92
|
mm/mm
|
| CD | 1 | mm/mm | ||
|
Murtovenymä
|
ISO 527-3
|
MD |
146,1
|
mm
|
| CD |
65,2
|
mm
|
||
|
Vetokuormitus
|
ISO 6383-1
|
MD |
0,30
|
N
|
| CD |
0,45
|
N | ||
|
Repäisylujuus
|
ISO 6383-1
|
MD |
20,5
|
N/mm
|
| CD |
30,2
|
N/mm
|
||
|
Vetolujuus
|
ISO 6383-1
|
MD |
0,82
|
MPa
|
| CD |
1,21
|
MPa | ||
|
Barrier-ominaisuudet
|
||||
|
Parametri
|
Standardi
|
Nimellisarvo
|
Yksikkö
|
|
|
WVTR
|
ASTM E 96
|
105
|
g/m2/24h | |
|
OTR
|
ASTM D 3985-5
|
1043
|
cm3/m2/24h
|
|
|
Lämpöominaisuudet
|
||||
|
Parametri
|
Standardi
|
Nimellisarvo
|
Yksikkö
|
|
|
Sulamispiste
|
ISO 3146
|
110
|
°C |
| Dimensions | ||||
| Parameter | Standard | Nominal value | Unit | Tolerance |
| Thickness | ISO 534 | 25 | mic | +/- 10% |
| Physico-mechanical properties | ||||
| Parameter | Standard | Nominal value | Unit | |
| Unit weight | ASTM D 2673 | 31,25 | g/m2 | |
| Density | ISO 1133 | 1,25 | g/cm³ | |
| Modulus (automatic Young's) | ISO 527-3 | MD | 4662 | MPa |
| CD | 4081 | MPa | ||
| Tensile stress at yield | ISO 527-3 | MD | 57,3 | MPa |
| CD | 54,0 | MPa | ||
| Tensile stress at tensile strength | ISO 527-3 | MD | 83,1 | MPa |
| CD | 53,5 | MPa | ||
| Tensile strain at tensile strength | ISO 527-3 | MD | 2,64 | mm/mm |
| CD | 0,08 | mm/mm | ||
| Tensile strain at break | ISO 527-3 | MD | 2,92 | mm/mm |
| CD | 1 | mm/mm | ||
| Tensile extension at break | ISO 527-3 | MD | 146,1 | mm |
| CD | 65,2 | mm | ||
| Load at tensile strength | ISO 6383-1 | MD | 0,30 | N |
| CD | 0,45 | N | ||
| Tear resistance | ISO 6383-1 | MD | 20,5 | N/mm |
| CD | 30,2 | N/mm | ||
| Tensile stress at tensile strength | ISO 6383-1 | MD | 0,82 | MPa |
| CD | 1,21 | MPa | ||
| Barrier properties | ||||
| Parameter | Standard | Nominal value | Unit | |
| WVTR | ASTM E 96 | 105 | g/m2/24h | |
| OTR | ASTM D 3985-5 | 1043 | cm3/m2/24h | |
| Thermal properties | ||||
| Parameter | Standard | Nominal value | Unit | |
| Melting point | ISO 3146 | 110 | °C |